Micava 128L self-leveling high polymer/ceramic composite is a two-component self-leveling epoxy ceramic composite material. The material is composed of high-performance epoxy resin and ceramic. Micava 128L has properties of long operating time, good leveling, excellent resistance to water, and outstanding wear resistance. Micava 128L has met the safety evaluation standards of drinking water equipment and protective material safety.
- Protect and repair all kinds of corrosion, cavitation erosion of pump, fans shell, impeller, hydropower stations valves, and turbine impeller
- Utilize the long operating time for large area protection
- Utilize the excellent resistance to water and outstanding wear resistance to improve pump efficiency
Operating temperature: 120℃ (Dry) 65℃ (Wet)
Hardness shore D (ASTM D-2240): 89
Tensile strength (ASTM D-638): 400 kg/ cm²
Compressive strength (ASTM D-695): 720kg/ cm²
Adhesive Strength (ASTM D1002): 240 kg/ cm²
Chemical Resistance Data:
Sodium hydroxide (0-50%) : E
Sodium chloride (0-30%) : E
Seawater : E
Deionized water: E
Ethanol : NR
*Notes: Samples cured 7 days before the test, the test time is 30 days at 25 ℃
E = Excellent (Can be long-term immersed)
G = Good (Can be occasionally sprinkled, but need to remove)
NR = Not Recommend (Cannot be adhered to, material will be damaged)
- Surface Treatment:
Sandblasting the steel surface with chlorine-free abrasive. For external application, the surface should reach SSPC SP-10 standard, close to the white metal treatment standard. After sandblasting the surface, repair surface as soon as possible to prevent surface oxidation, then repair the damaged area properly.
Resin :hardener mixed rate is 1:1.6 by weight.
Do not dilute.
- Application tools:
Use a plastic spatula or plaster knife.
- Application temperature:
Material temperature: Keep at 55-95℉ (13-35℃)
Substrate temperature: Keep at 45-105℉(7-40℃)
The temperature difference between the substrate and the coating must not exceed 10℉(5℃)
- Re-coating/curing time:
Recoating in the time when material were still soft, within two hours, at 77ºF (25ºC). If the recoating time has been exceeded, polish the surface with sandpaper, grinding, or blasting. Before immersion application, fully cured in 36 hours at 25 ºC. When heating to force curing, the best performance requires 1 hour at 93 ºC, or 12 hours at 49 ºC.
Wash with methyl ethyl ketone or similar products.